pros and cons of each? i like the ceramic..thinking of getting one. do i need one? i think i have a bucket full of random steels.
My experience exactly. Only occasionally use a steel on my softer French and German carbons. That being said, if available, I much prefer to strop on my felt and or a clean finishing stone depending on how far the edge has degraded and it works much much better than any steel ceramic or otherwise that I've used. I've lately been able to keep edges alive and kicking for a month or so in a pro environment using this technique.99% of grooved steels are junk, they can only (at best) rip the edge apart to offer some edge teeth to aid in cutting performance but when used on hard/thin edged Japanese knives the pressure exerted easily cause edge chipping.
A really hard & smooth steel would be a decent option for these knives (something like the slick made by F. Dick) but this only works OK since you need to use it often and catch the edge before it degrades too far.
A smooth ceramic rod, and to some extent a very fine diamond rod, is a compromise between those two above as they scrape the edge to provide some teeth but (in the case of the ceramic) it's more forgiving as to not chip the edge and both will work a lot longer than a smooth steel will.
In all cases I find them inferior to a nice strop but that's my own personal tastes talking, there're really nothing wrong with using a steel/rod if used correctly.
Since the point of a steel is to roll the edge back into shape after it's been deformed, there really is no comparison with a ceramic rod which is usually abrasive. A steel, when the edge is drawn straight across the steel, not forced into it, will restore most of an edge on a Western knife. On a Japanese knife, any significant pressure is likely to knock chips out, quite the opposite of restoring the edge.
There is no point in using a steel on a very hard knife since you cannot roll the edge back up anyway with any reliability. Probably a waste of time on a hard high carbon stainless knife too.
If you actually remove material with the steel, any really sharp edge is gone anyway.
Peter
No, never used a glass rod, just our ancient grooved steel (works great on carbon steel, so-so on high carbon stainless) and a ceramic rod that I didn't know how to use properly. Should be like a smooth steel, I'd think, unless it's not smooth, in which case I have no idea what it would do.
Peter