Yes, non-magnetic plus a tiny bit (basically ensure the entire blade won't stick...then look for the next tiny shade of color...should take a couple seconds or so). Quench in ice water that you've added some dawn to...as well as salt to until it won't dissolve anymore. IF there's carbon in it...that'll do the trick. Check for hardness with a file. Also...as he said, you shouldn't need to temper it.
I try to be the man I am..in times of broken lives. Shattered dreams and plans..standing up to fight. Pressures and demands..staring at the knife. Holding in your hands..
A tip for forging the tip in round bar. Forge a square sided point on the end, knock the corners off, forge to round. Then set your heel and choil and draw the taper into the tip. You will need to refine the tip shape as you go. Forging temperature in general, bright yellow, around 1150 degrees c. Try not to forge below a yellow heat unless you are surface finishing. Or it is needlessly hard work.
Blacksmith school most used phrase, "Get it hot"
You should refine the grain after forging however. Can be done in your pre-heat treatment by normalizing. Heat to non-magnetic 3 times checking straightness and air cooling.
Mailing List - http://www.catchesidecutlery.com/contact.html
Works in Progress - https://www.instagram.com/catcheside_cutlery/?hl=en
Did some grinding. Asymmetric right hand grind, single-bevel style right face with slightly convex(I was trying for flat) left face. I feel I should mention that I am doing all of the grinding on a 3400rpm bench grinder, as that is all I have to do the job. I will try to work on stones (and maybe files) only after the HT because this grinder would probably kill it pretty quickly.
Finished grinding for today. I will probably clean it up some before attempting to normalize and HT this unknown steel from the yard.
The tip was left thicker for now.
Thanks for all of the advice everyone.
A couple of updates.
I clamped a file to my stone holder and cut in the geometry. It is now flat on the left face and single-bevel style grind on the right face. I left the tip mostly unground still so it is not too thin during HT.
Sanded today to 220 grit on the back and table, the file left some deep scratches which I am just going to leave there, it's character.
I'm impressed. Good work!
If you're going through hell, keep going.
That looks really cool! Throw me in the impressed column.
Wow, that shined up nice. People sell things that look way worse for ridiculous amounts (see ugliest knife ever thread).
Thanks for the kind words, everyone.