Thread: Zombie Buschef Knife

  1. 03-13-2012, 07:11 AM #21
    apicius9
    apicius9 is offline
    Das HandleMeister apicius9's Avatar
    Join Date
    Feb 2011
    Location
    Honolulu, HI
    Posts
    3,484
    Great thread. Reminds me of that Koster knife I had a while ago. Looked great, but was more like a Bowie than a real kitchen knife... Look forward to seeing where this is going.

    Stefan
    www.japanesehandles.com
    Reply With Quote Reply With Quote
  2. 03-14-2012, 04:29 PM #22
    HHH Knives
    HHH Knives is offline

    HHH Knives's Avatar
    Join Date
    Apr 2011
    Location
    Michigan
    Posts
    4,172
    It looks like tomorrow or Friday I will be Heat Treating this blade and a few others. Im not sure what I will do for the handle yet. But probably will do it up nice for ya is the blade hardens.

    Inspired by God, Forged by Fire, Tempered by Water, Grounded by Earth, Guided by the spirit.. Randy Haas

    Availible Knives
    Reply With Quote Reply With Quote
  3. 03-14-2012, 08:56 PM #23
    Crothcipt
    Crothcipt is offline
    Senior Member Crothcipt's Avatar
    Join Date
    Jan 2012
    Location
    wyoming, closer to nowhere than somewhere.
    Posts
    3,483
    Man you are busy, which is good to hear. Man I can't wait to see what you come up with. I usually don't get excited but this is blowing me away.
    Reply With Quote Reply With Quote Thread Starter 
  4. 03-17-2012, 01:55 AM #24
    Crothcipt
    Crothcipt is offline
    Senior Member Crothcipt's Avatar
    Join Date
    Jan 2012
    Location
    wyoming, closer to nowhere than somewhere.
    Posts
    3,483
    Ok I am chomping at the bit to know how Heat Treating went. Did it melt all over the oven like I think it would? Pleas throw me a bone...
    Reply With Quote Reply With Quote Thread Starter 
  5. 03-17-2012, 02:19 AM #25
    HHH Knives
    HHH Knives is offline

    HHH Knives's Avatar
    Join Date
    Apr 2011
    Location
    Michigan
    Posts
    4,172
    Hang in there. I didnt get a chance to HT the blade today. Im thinking tomorrow afternoon maybe.

    That is if it doesn't melt!!!

    Inspired by God, Forged by Fire, Tempered by Water, Grounded by Earth, Guided by the spirit.. Randy Haas

    Availible Knives
    Reply With Quote Reply With Quote
  6. 03-17-2012, 02:51 PM #26
    HHH Knives
    HHH Knives is offline

    HHH Knives's Avatar
    Join Date
    Apr 2011
    Location
    Michigan
    Posts
    4,172
    Today was the day. I started the HT process on this knife! First I had to anneal it and ran it through a couple of normalization cycles. Trying to make the steel as ready as possible for the quench!

    Believe it or not. HT went well. I took the blade up to temp, and held for about 5 minutes. Then quenched the blade in oil. And guess what, It didnt explode or delam or warp etc. seemed to HT well as far as I can tell at this point. And Is straight as a arrow.

    Its not in the first of 2 temper cycles..

    Here are a few pictures. I am working alone today. so I didnt get photos on the quench or clean up etc.
    Attached Thumbnails Attached Thumbnails Click image for larger version.  Name: IMG_7136.JPG  Views: 56  Size: 282.1 KB  ID: 5394   Click image for larger version.  Name: IMG_7142.JPG  Views: 66  Size: 313.0 KB  ID: 5395  

    Click image for larger version.  Name: IMG_7146.JPG  Views: 65  Size: 339.7 KB  ID: 5396  
    Attached Images Attached Images  

    Inspired by God, Forged by Fire, Tempered by Water, Grounded by Earth, Guided by the spirit.. Randy Haas

    Availible Knives
    Reply With Quote Reply With Quote
  7. 03-17-2012, 11:33 PM #27
    Crothcipt
    Crothcipt is offline
    Senior Member Crothcipt's Avatar
    Join Date
    Jan 2012
    Location
    wyoming, closer to nowhere than somewhere.
    Posts
    3,483
    wow. Just by how the metal acted, when I had it home I would have thought this would have been more of a problem than what it turned out to be. Thx for the pics.
    Reply With Quote Reply With Quote Thread Starter 
  8. 03-18-2012, 12:42 AM #28
    Taz575
    Taz575 is offline
    Join Date
    Jan 2012
    Location
    CT
    Posts
    468
    It's ALIVE!! Isn't think disproving the old idiom that you can't make a silk purse out of a sows ear??
    Reply With Quote Reply With Quote
  9. 03-18-2012, 09:54 AM #29
    HHH Knives
    HHH Knives is offline

    HHH Knives's Avatar
    Join Date
    Apr 2011
    Location
    Michigan
    Posts
    4,172
    Dont get ahead of me on this one guys.. It did make it through the quench.. And after its quenched I tempered it. and then I tested it for hardness.

    My initial tests are bad! Very low RC.. It is SO LOW that its softer then the test equipment that I use even goes.. I dont know what kind of steel they used.. but Its is not High Carbon steel, let alone 1095 like they claimed.. or I would of been able to get it to harden..


    Am I surprised. NO


    More to come later.

    Inspired by God, Forged by Fire, Tempered by Water, Grounded by Earth, Guided by the spirit.. Randy Haas

    Availible Knives
    Reply With Quote Reply With Quote
  10. 03-18-2012, 03:08 PM #30
    Eamon Burke
    Eamon Burke is offline
    Join Date
    Mar 2011
    Location
    Rockport, TX
    Posts
    4,879
    Could it be that it had a very small core of 1095, and that damascus cladding is made from low carbon stuff?
    Reply With Quote Reply With Quote