    Quote Originally Posted by ajhuff View Post
    JB Weld.
    -AJ


    Inspired by God, Forged by Fire, Tempered by Water, Grounded by Earth, Guided by the spirit.. Randy Haas

    Availible Knives

  2. #22
    Senior Member

    Join Date
    Feb 2011
    Location
    San Diego, CA
    Posts
    4,227
    Amazing! Sorry, Chuck!

  3. #23
    Senior Member Crothcipt's Avatar
    Join Date
    Jan 2012
    Location
    wyoming, closer to nowhere than somewhere.
    Posts
    3,501
    Just curious at what they look like where the split is. And what are you gonna do with them?

  4. #24
    Sponsors

    Bill Burke's Avatar
    Join Date
    Mar 2011
    Location
    Lives in the mountains near Boise, Idaho.
    Posts
    495
    Quote Originally Posted by Crothcipt View Post
    Just curious at what they look like where the split is. And what are you gonna do with them?
    Not exactly sure what you mean. But it looks like a nice clean satin break Probably just going to leave it hanging around the shop for a show and tell thing.

  5. #25
    Senior Member Crothcipt's Avatar
    Join Date
    Jan 2012
    Location
    wyoming, closer to nowhere than somewhere.
    Posts
    3,501
    What I was meaning was the sides of were the 2 pieces used to meet. Its probably nothing to see. You only have a pic. from the top.

  6. #26
    Sponsors

    Bill Burke's Avatar
    Join Date
    Mar 2011
    Location
    Lives in the mountains near Boise, Idaho.
    Posts
    495
    OK that is what i was thing but wasn't sure. looks like a nice fine grained break. I'll see if I can get a picture.

  7. #27

    Join Date
    Jul 2011
    Location
    St. Petersburg, FL
    Posts
    1,297
    DANG!!!! I tried welding up 416 and Cru Forge and it just never stuck, but that is funky the away the core split. I think I recall one of the guys who does that a lot saying that you might want to clay up the spine on those laminates because the do get stressed all to hell in the quench. Derrick Wulf made a san mai blade recently using 304 as the cladding instead of 416 and he says it welds a lot easier. It also isn't martensitic steel , so I wonder if it gets stressed out less.

  8. #28
    rhygin's Avatar
    Join Date
    Apr 2011
    Posts
    25
    The fact that it crack is so symmetrical is really interesting. It seems improbable the the stresses would be so balanced and that the core steel would be the weaker element. As far as I'm concerned, this is an endorsement of your method (ignoring the obvious), that you can create something so balanced.

  9. #29
    Sponsors

    Bill Burke's Avatar
    Join Date
    Mar 2011
    Location
    Lives in the mountains near Boise, Idaho.
    Posts
    495
    When I first started doing this laminate in 2002 I was talking with Daryl Myer and was told by him that this could and would happen. According to Daryl it is far more likely to happen with 300 series stainles than with the 400 series that I use and the reason that I use it in the first place. For those of you who don't know who Daryl Myer is Pretty much every modern pattern welding technique that we use in some way belongs to Daryl.

  10. #30
    Weird Wood Pusher Burl Source's Avatar
    Join Date
    Jun 2011
    Location
    Kerby, OR
    Posts
    3,463
    I think you have a great piece of modern art there.
    Now you just have to figure how you will display your new sculpture.

    Mark Farley / It's a Burl
    Phone 541-592-5071, Email burlsource@gmail.com
    Visit our web store

+ Reply to Thread

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts