Quantcast
BB @ EE - Page 4
Page 4 of 5 FirstFirst ... 2345 LastLast
Results 31 to 40 of 41

Thread: BB @ EE

  1. #31
    Senior Member

    Join Date
    Feb 2011
    Location
    Pensacola, FL, USA
    Posts
    3,993
    Beautiful work, Bill.

  2. #32
    Sold to a lucky customer

    Damn that was a beauty!

  3. #33
    Senior Member mattrud's Avatar
    Join Date
    Mar 2011
    Location
    NYC
    Posts
    551
    Quote Originally Posted by Bill Burke View Post
    Matt if I were a real tease I would tell you that there is a new sanmai 240mm gyoto up and maybee post a link like this.

    Attachment 6334
    Bill, Seriously that is just awesome. I mean really Bill I don't know what else to say. Except maybe I like you horn handles better.

    One day I will have one, one day.

  4. #34
    Senior Member Lucretia's Avatar
    Join Date
    Oct 2011
    Location
    Isle of Lucy
    Posts
    1,618
    Oivind,

    Have you seen the musk ox paring knives now at EE? They look like they'd go beautifully with your collection.

  5. #35
    Thanks however mr BB is soon to start on mine now and one of those is a parer and i cannot afford anoher for the next ten years.

  6. #36

  7. #37
    Bill, I'm curious, especially as 15n20 and 1080 steels are used so often for damascus -- which of those two steels do you think makes a better monosteel knife, especially for kitchen use?
    Tom Gray, Seagrove, NC

  8. #38
    Ive googled and don't find that out. I see a lot of MS favorite 52100 for monosteel. But 52100 is an animal; it doesn't play well with others, hell it doesn't play well with its own and as I understood from a post of Ed Caffrey, it reacts very poorly to overheating (is this why integrals are a pita on forge welding on 52100?)
    http://knifedogs.com/archive/index.php/t-18858.html?

    Why will you have a blade in 15n20 or 1080, when there are so many really great steels out there?

  9. #39
    Because 1080 and 15n20 are much easier for us newbie knife makers that don't want to send our blades out for heat treat. If anyone really familiar with HT wants to jump in here, please do.
    Tom Gray, Seagrove, NC

  10. #40


    Bill Burke's Avatar
    Join Date
    Mar 2011
    Location
    Lives in the mountains near Boise, Idaho.
    Posts
    510
    of the two steels that you mention I would choose 15n20 for a monosteel knife. I have found that it is a very good steel on its' own with a good heat treat.