    1,632
    Ha ha, probably no danger of that But I wont be happy until i've worked out the parameters a bit more.
    This is a datasheet with some micrographs under different HT conditions.
    http://www.kmts.co.za/stores/afri-th...ta%20sheet.pdf
    Over soaking or under soaking at temperature would cause a loss of potential hardness, so I can test for that in more detail on a tapered piece.
    I'm pretty sure these tested the same near the tip as to the heel.

  2. #12
    Senior Member
    Join Date
    Feb 2011
    Location
    San Diego, CA
    Posts
    4,214
    Quote Originally Posted by ajhuff View Post
    I KNOW it's not AEB-L but I dropped my Geshin Ginga...
    How do you know?

    @Will: If you mean a brass rod test, no. However, Niolox at 62 hrc "seems" more brittle to me. It's been a while but I believe I've lost a tip or two on Niolox. The AEB-L blades I have tend to deform when they get tipped. I don't know if that is a characteristic of the steel or that particular HT.

  3. #13

    Join Date
    May 2011
    Location
    Top of Georgia
    Posts
    1,218
    I don't know what it is made of. Moot point.

    -AJ