Smidderton
Well-Known Member
20 cm x 4,7 cm
177 Grams
Spine at Handle: 0,6 cm
34,8 cm length overall
13,1 cm Handle length, burnt oak
SC125 / wrought iron
The P stands for prototype. This was about the hardness - 65 hrc in this case - of the sc125 in combination with the wrought iron.
440 400€ - EU shipping prefered. But will ship worldwide.
The iron is pretty clean. You only really see the inclusions when freshly polished.
History:
I got this directly from Bryan. Originally it had a rough satin finish. I removed that because I wanted to see more of wrought iron.
Current finish is 8k Naniwa. Would'nt call it kasumi though... this is my first time polishing. Did'nt have a lot of patience.
I kept the edge sharp with 8k naniwa and 5k shapton.
2mm tip broke off in cauliflower. I repaired that on stones. Edge was 20,2cm before, now it's 20cm.
In the Naniwa-Video you see the current condition. The pics are pre-polish and show the knife how it looks like when used.
177 Grams
Spine at Handle: 0,6 cm
34,8 cm length overall
13,1 cm Handle length, burnt oak
SC125 / wrought iron
The P stands for prototype. This was about the hardness - 65 hrc in this case - of the sc125 in combination with the wrought iron.
The iron is pretty clean. You only really see the inclusions when freshly polished.
History:
I got this directly from Bryan. Originally it had a rough satin finish. I removed that because I wanted to see more of wrought iron.
Current finish is 8k Naniwa. Would'nt call it kasumi though... this is my first time polishing. Did'nt have a lot of patience.
I kept the edge sharp with 8k naniwa and 5k shapton.
2mm tip broke off in cauliflower. I repaired that on stones. Edge was 20,2cm before, now it's 20cm.
In the Naniwa-Video you see the current condition. The pics are pre-polish and show the knife how it looks like when used.
Last edited: