Can any of the smiths here comment on whether it is a good idea to do as much open air forging on ZDP laminates as their website claims, or whether that will actually wreck the steel? From what I head about PM steels, doing so seems like boiling chocolate and then expecting it to cool to perfect temper. I mean, ZDP would be cast iron if you let it do what it wants?