I'm not sure what you mean by this, but it's looking pretty good to me so far!...am wondering if swinging a bit too far...
Thanks. Am aiming for a 70:30 but forgot to mark the blade. D'oh!I'm not sure what you mean by this, but it's looking pretty good to me so far!
Keep going!
That is post heat treat, lots of grind then dunk.Looks like good progress to me.
Like you already mentioned some layout fluid and scribe lines would have helped out a ton.
But a quick question comes to mind. Is this your pre-heat treat grind or is the blade already heat treated?